HTM1401V Specifications*
Tensile Strength Elongation at Break Flexural Strength Flexural Modulus HOT (Heat Deflection Temperature) No heat treatment necessary Colors Available View Full Specifications
56 MPa 3.5% 115 MPa 3350 MPa 140°C (284°F) Ivory Download PDF
HTM140 Specifications*
Tensile Strength Elongation at Break Flexural Strength Flexural Modulus HOT (Heat Deflection Temperature) No heat treatment necessary Colors Available View Full Specifications
56 MPa 3.5% 115 MPa 3350 MPa 140°C (284°F) Green Download PDF
PIC100 M/PIC100G M Specifications*
DIN 1342-2 DIN EN ISO 527-1 DIN EN ISO 178 DIN EN ISO 180 DIN ISO 1183-1 DIN EN ISO 868 DIN 53765 View Full Specifications
Viscosity361.7 mPa*s Tensile Strength
Elongation at Break16.8 MPa
7.46%
Flexural Strength
Flexural Modulus
Bending Strain23.0 MPa
404.0 MPa
10.2%
lzod Impact-Notched11.03 kJ/m2 Density1.178 g/cm3 Hardness (Shore D)69 Shore Ignition Temperature350 oc Download PDF
PIC100/PIC100 G Specifications*
DIN 1342-2 DIN EN ISO 527-1 DIN EN ISO 178 DIN EN ISO 180 DIN ISO 1183-1 DIN EN ISO 868 DIN 53765 View Full Specifications
Viscosity361.7 mPa*s Tensile Strength
Elongation at Break16.8 MPa
7.46%
Flexural Strength
Flexural Modulus
Bending Strain23.0 MPa
404.0 MPa
10.2%
lzod Impact-Notched11.03 kJ/m2 Density1.178 g/cm3 Hardness (Shore D)69 Shore Ignition Temperature350 oc Download PDF
RC70 Specifications*
DIN EN ISO 527-1 DIN EN ISO 527-1 DIN EN ISO 178 DIN EN ISO 178 ASTM D 648 View Full Specifications
Tensile Strength39 MPa Elongation at Break2.9% Flexural Strength106 MPa Flexural Modulus3760 MPa Heat Deflection Temp. (at
0.46 MPa)93 °c
Download PDF
RC90 Specifications*
DIN EN ISO 527-1 DIN EN ISO 527-1 DIN EN ISO 178 DIN EN ISO 178 ASTM D 648 View Full Specifications
Tensile Strength38 MPa Elongation at Break2.7% Flexural Strength104 MPa Flexural Modulus3800 MPa Heat Deflection Temp. (at
0.46 MPa)73 °c
Download PDF
WIC100G Specifications*
DIN 1342-2 DIN EN ISO 527-1 DIN ISO 1183-1 DIN EN ISO 868 DIN 53765 View Full Specifications
Viscosity4.200 cps Tensile Strength
Elongation at Break14.8 MPa, 6.3%
Density1.32 g/cm3 Hardness (Shore D)80 Shore Ignition Temperature300 o c Download PDF